Boron • Metalloid

Primary XPS region: B1s
Overlapping regions: Si2s plasmon, P2s, Zr3d
Binding energies of common chemical states:

Chemical stateBinding energy
B elemental187.2 eV
ZrB2187.8 eV
B sub-oxide[1]188.6 eV
Li2B4O7192.5 eV

Charge referenced to adventitious C1s peak at 284.8eV.

 

Experimental information

  • B1s peak has very low sensitivity.
    • Use a large number (50) of scans when acquiring B1s spectrum if boron is present in low concentrations.

 

Interpretation of XPS spectra

  • When boron is implanted in silicon, the strong Si2s plasmon loss feature strongly overlaps the B1s region.
    • Restricts detection of low concentrations of boron implanted in silicon.
    • Detection limit for boron in silicon is 7×1020 atoms cm-3.
      • Actual detection limit depends on implantation depth (more readily visible at surface).
Boron • Metalloid
Interpretation of XPS Spectra
 
  • In the example shown above, the Si2s plasmon has been empirically fitted (this does not represent a theoretically rigorous treatment of the plasmon shape).
  • It is difficult to confidently assign B1s peak for low concentrations when no secondary peak is observed.
    • For high enough concentrations of boron, the B KLL Auger peak will be observed.
X-Ray Induced B KLL spectrum of elemental boron

General comments

  • Elemental boron samples are usually oxidized at the surface.
    • May observe sub-oxide rather than B2O3.

 

References

  • [1] Ong et al., J. Appl. Phys., Vol. 95, No. 7, 1 April 2004.

 

element-crystal-rhom

About this element

Symbol: B
Date of discovery: 1808
Name origin: Arabic buraq
Appearance: brownish
Discoverer: Sir Davy, et al.
Obtained from: kernite

Melting point: 2349 K
Boiling point: 4200 K
Density[kg/m3]: 2460
Molar volume: 4.39 × 10-6 m3/mol
Protons/electrons: 5
Neutrons: 6
Shell structure: 2,3
Electron configuration: [He]2s22p1
Oxidation state: 3
Crystal structure: rhombohedral

Although compounds of boron have been known for thousands of years, the element itself was not isolated until Sir Humphry Davy, Gay-Lussac, and L.J. Thenard isolated it to about 50% purity in 1808. Jöns Jacob Berzelius later identified boron as an element in 1824 and American chemist, W. Weintraub, produced pure boron for the first time in 1909. Boron is not found in its elemental form in nature, but is found in compounds. Compounds of boron have many applications: they are used in making insulating fiberglass, sodium perborate bleach, pyrotechnic flares, and making high-strength, lightweight materials primarily important for advanced aerospace structures.

 


Products

Nexsa G2 XPS

  • マイクロフォーカスX線源
  • 独自の追加可能なオプション
  • 単原子およびクラスターイオンデプスプロファイリング用のデュアルモードイオン源
Style Sheet for Instrument Cards Origin

K-Alpha XPS

  • 高分解能XPS
  • 高速で効率的な自動ワークフロー
  • イオン源を用いたデプスプロファイリング

ESCALAB Xi+ XPS

  • 高いスペクトル分解能
  • マルチテクニックによる表面分析
  • 試料作製および拡張のための豊富なオプション

Contact us

Style Sheet for Global Design System
Style Sheet for Komodo Tabs
Style Sheet to change H3 to p with em-h3-header class
Style Sheet to change H2 style to p with em-h2-header class
Style Sheet for Products Table Specifications
Style Sheet for Global Design System
Style Sheet for Komodo Tabs
Style Sheet to change H3 to p with em-h3-header class
Style Sheet to change H2 style to p with em-h2-header class
Style Sheet for Products Table Specifications
Fix for left nav
Style Sheet for Support and Service footer
Style Sheet for Fonts
Style Sheet for Cards

材料科学向けの
電子顕微鏡サービス

最適なシステム性能をお届けするため、当社は国際的なネットワークで、分野ごとのサービスエキスパート、テクニカルサポート、正規交換部品などを提供しています。